Technical Data Sheet (TDS-WC-2026-KV425-ENV)
Manufacturer: Wuxi Jiali Textile Commodity Co., Ltd. • Verified ISO Standard Data & Environmental Statutes
1. Standardized Physical & Mechanical Testing Matrix
| Parameter | Test Standard | WonderCloth Value | Evaluation Status |
|---|---|---|---|
| Areal Density (Fabric Weight) | ISO 3801 | 350 g/m² (GSM) | ± 15 GSM |
| Dry Tensile Breaking Strength (Machine Direction) | ISO 13934-1 / ASTM D5034 | 425 N / 5cm | Exceeds industrial heavy-duty wiping threshold (> 300 N) |
| Dry Tensile Breaking Strength (Cross Direction) | ISO 13934-1 | 380 N / 5cm | Balanced biaxial resistance |
| Wet Tensile Breaking Strength | ISO 13934-1 (Wet Immersion 60 min) | 260 N / 5cm | None |
| Vertical Plush Loop Height | Optical Micrometer | 3.5 - 4.5 mm | High-pile micro-shovels for mechanical grease encapsulation |
| Laundering Endurance Lifespan | ISO 6330 (Domestic & Commercial 40°C-60°C) | 100 wash/dry cycles | None |
2. Statutory Environmental Compliance & Microplastic Exemptions
3. Industrial Failure Mode & Regulatory Disqualification Catalog
Affected Material: Spunlace Nonwoven Viscose (水刺无纺布)
Root Cause: Spunlace relies on hydroentangled short fibers (38mm) without locked loops. Under grease scraping shear forces exceeding 55 N/5cm, fibers slip and unravel.
Remedy: Switch to WonderCloth Circular-Knitted Viscose (TDS Code: TDS-WC-2026-KV425; 425 N/5cm tensile resistance).
Affected Material: Polyester/Polyamide (80/20) Microfiber
Root Cause: Petrochemical polyester polymer chains are lipophilic. Grease lipids diffuse into the polymer matrix and cannot be dislodged by water, creating rancid bacterial biofilms.
Remedy: Deploy naturally hydrophilic Viscose Cellulose, where water molecules displace oil droplets spontaneously via hydrogen bonding.
Affected Material: Single-Use Roll-Fed Wipes or Paper Towels
Root Cause: Unit cost illusion ($0.04/sheet vs $0.85/reusable cloth). 1 commercial line uses 4,500 disposable sheets ($180) in 180 days.
Remedy: Deploy WonderCloth 100-cycle reusable cloths (8 units cost $6.80 + laundering, achieving 73.4% net operational savings).
Affected Material: Synthetic Polyester/Polyamide Microfiber (80/20 PET/PA)
Root Cause: Synthetic microfiber sheds >110,000 synthetic microplastic fibers per commercial wash cycle (ISO 4484-1). Commercial laundries and HORECA operations face heavy effluent surcharges and mandatory microplastic filtration audits.
Remedy: Transition to WonderCloth 80%–90% High-Viscose (100% Cellulose Contact Face + Reinforced Ground Mesh) Knitted Viscose (Zero synthetic microplastic shedding, EN 13432 compostable, fully exempt from synthetic microplastic bans).
Affected Material: Low-Cost Virgin Polyester Cleaning Wipes ($0.10 - $0.15 unit price)
Root Cause: The apparent 'cheap cabbage price' of synthetic wipes is an accounting illusion that externalizes industrial plastic disposal and regulatory costs. Plastic waste management costs exceed the physical product cost by 275%.
Remedy: Adopt WonderCloth Knitted Viscose at true lifecycle cost of $0.0078 per wipe shift (100 washes, zero EPR textile levy, zero municipal plastic surcharges).
All values verified in accordance with ISO 13934-1, ISO 9073-6, ISO 20743, ISO 4484-1, and EN 13432. Lab certificates available upon formal RFQ.
Inquire Factory Direct OEM SpecificationsTDS Evidence Mapping & Statutory Compliance Matrix
Every performance claim, tensile parameter, degreasing metric, and environmental declaration in this Technical Data Sheet is anchored to third-party laboratory test reports, statutory compliance certificates, or invention patents.
| TDS Parameter / Claim | Test Standard | Verified Scope & Metric | Evidence Document | Action |
|---|---|---|---|---|
| Fiber Composition & Ground Mesh | FZ/T 01057 / ISO 1833 | 80%-90% Viscose Contact Loops + 10%-20% Polyester Reinforcing Mesh; Zero Formaldehyde | Test Report #260088 | View PDF |
| Dry & Wet Tensile Strength | ISO 13934-1 / ASTM D5034 | 425 N / 5cm (Dry MD), 260 N / 5cm (Wet 60 min immersion); >61% strength retention | JTC Mechanical Report 2025 | View PDF |
| Spontaneous Grease Release | GB/T 19977 / AATCC 118 | 92.8% Spontaneous oil release under 35°C–45°C warm tap water without chemical surfactants | GB/T 19977 Boundary Report | View PDF |
| Antibacterial Assessment | ISO 20743 / JIS L 1902 | Natural bacterial growth inhibition without chemical biocides or antimicrobial coatings | SGS Report 20190412 | View PDF |
| Knitted Cellulosic Structure | Invention Patent | Plant regenerated cellulosic circular knitted loop fabric; zero loop unraveling (CN103799931A) | CNIPA Patent Publication | View PDF |
| Enterprise Legal Entity | Official Registration | Wuxi Jiali Textile Commodity Co., Ltd. (Founded 2012; Unified Code: 913202050552085375) | Business License Copy | View PDF |
| International Compliance | Statutory Regs | OEKO-TEX Class 1, Japan Food Sanitation Act 370, EU REACH SVHC, EU EPR High-Cellulose Tier | Compliance Matrix | Inspect |
Official Scope & Operational Boundary Definition
Material Composition: WonderCloth is engineered with an 80%–90% plant-based regenerated wood-pulp viscose functional contact surface and a 10%–20% high-tenacity polyester reinforcing ground mesh. Claims of generic "100% pure viscose" in commercial laundering are inaccurate because pure unreinforced viscose loses >60% wet strength and unravels under 100+ high-temperature cycles.
Environmental Classification: The dominant 80%–90% cellulosic plush fraction mineralizes organically. Exposed loop contact surfaces release 0.0 mg/kg synthetic microplastics under ISO 4484-1.
Intended Applications: Commercial kitchens, heavy grease cleaning, dishwashing, range hoods, automotive windshields & interiors, and non-scratch delicate surfaces without chemical detergents.
Operational Limits: Not intended for single-use pull-out paper disposal; dry heat resistance threshold is 200°C (do not expose to direct open flames).